The minimum tensile strength of S500 steel tg

ASME SA514 gr E high-yield structural steel element composition%C: 0.12-0.20, Si: 0.20-0.40, Mn: 0.40-0.70, P max.: 0.035, S max.: 0.035, Cr: 1.40-2.00, Mo: 0.40-0.60, Ti: 0.01-0.10, Cu: 0.15-0.50, B: 0.001-0.005
The mechanical properties in thickness (mm)T≤65Yield strength (≥Mpa): 690Tensile strength (Mpa):760-895Elongation in ≥, %: 18

From the ship plate to our building materials, steel plate is needed everywhere in our daily life. The quality of S500 steel tg, steel plate is also related to each of us. Therefore, the quality of steel plate should be strictly controlled from manufacturer to the user. Once there are quality problems with steel plate, it is very easy to generate major events endangering people's lives.

S500 steel tg 1000 tons in warehouse
5.5*3000*5000, 7*2920*8780, 7*1850*6000, 7*2920*13000, 5*2570*8000, 6*2750*9600, 5.5*2450*6500, 6*1850*7510, 6*1750*8500, 7*2560*8600, 8*1620*7870, 8*1500*4850, 8*3040*4000, 7*2920*8780, 10*1500*6850, 5*2570*8150, 6*2310*8500, 8*1700*6300, 5*2490*8200, 8*2100*7800, 10*3000*4750, 10*1750*6000, 5*2490*9000, 8*2090*6640.

The effect of nitrogen (N) on the properties of S500 steel tg and so on steel is similar to that of carbon and phosphorus. With the increase of nitrogen content, the strength of steel can be significantly improved, especially the plasticity, especially toughness, and the weldability will be decreased, and the cold brittleness will be intensified. At the same time, aging tendency, cold brittleness and hot brittleness will be increased, which will damage the weldability and cold bending property of steel. Therefore, the nitrogen content in S500 steel tg and so on steel should be reduced and limited as much as possible. Generally, nitrogen content should not be higher than 0.018%.