Welcome to BBN High Strength Steels Factory

Heat treatment process and purpose of S690QL thickness

Our company attaches great importance to technical support and after-sales service, and has established a customer service center to provide unified technical support and service for S690QL thickness various engineering projects. Customer service center has a strong technical force of technical service team, composed of a customer service center manager, several S690QL thickness after-sales service personnel, responsible for unified acceptance and processing of local after-sales service needs.

S355J0 steel is a low alloy structural steel. We can supply S355J0 structural steel plates up to 400mm, with a minimum yield strength 355MPa when plate thickness less than 16mm, min. yield strength 345MPa when plate thickness range 16mm to 40mm. Without any special rolling or heat treatment for S355J0 steel plate and sheet, S690QL thickness, the abbreviated designation of this delivery condition shall be AR (As rolled).

Weathering steel generally adopts the process route of fine material into the furnace-smelting (converter, electric furnace-microalloying treatment-argon blowing-LF refining-low superheat continuous casting (feeding rare earth wire)-controlled rolling and cooling. The scrap steel is added into the furnace together with the charge, and smelted according to the conventional process. After the S690QL thickness steel is tapped, deoxidizers and alloys are added. After the molten steel is treated with argon blowing, the molten steel is cast. By adding rare earth elements to the steel, the S690QL thickness weathering steel is purified and the content of inclusions is greatly reduced.

S690QL thickness, S235JR VS S275JR VS S355JR plates in yield strength: For plate thickness ≤16mm, the min. yield strength of S235JR plates is 235 Mpa, S275JR plates is 275 Mpa, S355JR plates is 355 Mpa. The yield strength of S235JR S275JR S355JR plates reduces with the increasing of plate thickness. S235JR VS S275JR VS S355JR plates in tensile strength: For plate thickness 3-100mm, the tensile strength of S235JR plates is 360-510 Mpa, S275JR plates is 410-560 Mpa, S355JR plates is 470-630 Mpa. For plate thickness 100-150mm, the tensile strength of S235JR plates is 350-500 Mpa, S275JR plates is 400-540 Mpa, S355JR plates is 450-600 Mpa.

Accept the inquiry from the owner of the goods and the inquiry by sea: master the port and price from the port of shipment to all continents and routes, and the port and price that the owner often needs to serve; the shipping schedule information of the main shipping companies; when necessary, ask the owner of the inquiry for some category information, such as the name of the goods, the level of danger, etc. (water hazard code).

The steel plate, steel pipe and other steel materials are the important material in the material engineers. Our company will provide the high quality the steel plate, steel pipe and other steel materials for you. We are exported the steel plate, steel pipe and other S690QL thickness steel materials to the customers from USA, South America, Europe, Africa etc. If we can have the good cooperation together, you will be very welcome to be our agent in your local market. Let’s work together!

Tags:

Leave a Message

EN 10025-6 S690QL High Strength Steels