The copper brittleness defects control of S690QL1 specification

High quality steel sheet and plate product S690QL1 specification supply 10.5*1970*7950, 13*1300*4350, 11*1900*12500, 12.5*2870*7100, 11*1870*12500, 10.5*1970*8000, 13*1520*7950, 11*1910*9000, 12.5*2900*8250, 11*1870*13500, 10.5*2350*6200, 14*1440*6100, 11*3100*10000, 13*1510*4850, 11*1870*9300, 11*1570*12000, 14*1800*9750, 11.5*2640*7600, 13*2380*6000, 11*2400*10000.

Since the welding process is often used in the fabrication and processing of steel structures, it is very important for low-alloy high-strength steels of such purpose to be welded using the arc welding process that is widely used in thin thickness plates and steel strips. Yes, the welding seam of the steel structure should have the required strength and toughness, so as to withstand the most unfavorable conditions for the intended use. At present, the development of S690QL1 specification, low-alloy high-strength steels is carried out simultaneously with the development of various welding processes. Most low-alloy high-strength steels can be welded well.

The effect of nitrogen (N) on the properties of S690QL1 specification and so on steel is similar to that of carbon and phosphorus. With the increase of nitrogen content, the strength of steel can be significantly improved, especially the plasticity, especially toughness, and the weldability will be decreased, and the cold brittleness will be intensified. At the same time, aging tendency, cold brittleness and hot brittleness will be increased, which will damage the weldability and cold bending property of steel. Therefore, the nitrogen content in S690QL1 specification and so on steel should be reduced and limited as much as possible. Generally, nitrogen content should not be higher than 0.018%.

Aspire to technological innovation and pursue first-class quality steel S690QL1 specification products.Take independent innovation as an important support for the sustainable development of iron and steel industry, strengthen the main position of technological innovation, accelerate the original innovation, integrated innovation, introduction, digestion, absorption and re innovation, improve the technological innovation system, and cultivate the core technology and brand products of independent intellectual property rights.