What is the notice of preheating before S690QL material specification cutting

The advantages of S690QL material specification, seamless steel pipe are high pressure resistance, good toughness, long pipe section and few joints. It is widely used and the rolling technology of domestic steel mills is also very mature. Compared with round steel, the weight of seamless steel pipe is lighter under the same strength. Seamless steel pipe manufacturing ring parts, can improve the utilization of materials, simplify the manufacturing process, save materials and processing time. Compared with the welded pipe, there is no weld on the outer surface of seamless steel pipe, and it has good compression resistance.

BBN steel S690QL material specification 15mm to 35mm thick size: 15*2120*5620, 17.5*2320*13000, 18*2450*5500, 20*3000*5000, 19*2580*4700, 19.5*1970*4000, 20*1600*7740, 20.5*2370*7000, 21*2650*7500, 21*1920*8220, 22*1380*7650, 22*1800*8000, 22.5*1680*8450, 23*3000*11980, 23.5*2080*8100, 24*1560*6200, 25.5*2330*8300, 26*3010*8100, 26.5*2000*7000, 27*2550*6800, 27.5*2700*5500, 29*2550*9000, 29*2870*12000, 32*3300*6000, 33*2340*6700, 34*2120*6100, 35*1300*4100.

Established in 2014, Steel Safety Day was set up to reinforce awareness of the five most common causes of safety incidents and to create a safer working environment across the entire steel industry worldwide. By focusing every year on the five causes - moving machinery, working at heights, falling objects, on-site traffic and S690QL material specification process safety incidents - worldsteel intends to set up a continuous improvement process and reiterate its commitment to the safety and health of the people who work in the S690QL material specification industry.

Oxygen (O) is a harmful element in steel such as S690QL material specification. Although manganese, silicon, iron and aluminum are added to deoxidize the steel at the end of steelmaking, they can not be removed completely. During the solidification of molten steel, the reaction of oxygen and carbon in the solution will produce carbon monoxide, which can cause bubbles. Oxygen mainly exists in the form of FeO, MnO, SiO2, Al2O3 and other inclusions in the steel, which reduces the strength and plasticity of the steel. Especially, it has serious influence on fatigue strength and impact toughness.