S460QL steel equivalent for lower than ambient temperature service

Heat-resistant steel thick plate is made of heat-resistant steel and is processed by hot rolling. According to different structure characteristics, it can be divided into four types: austenitic type, ferrite type, martensite type and precipitation hardening type. S460QL steel equivalent, The heat-resistant steel plate is widely used in the manufacture of petroleum, chemical equipment, boilers, steam turbines, industrial furnaces and other components and other components working at high temperatures.

Our company specializes in the production of steel plates, steel coil, steel sections, welded pipes and seamless pipes products, sales of GB, ASME, ASTM, JIS, DIN, EN, API and other standards and specifications of steel S460QL steel equivalent and deep-processed products, facing the domestic and foreign markets, welcome to call for inquiries. It is a modern high-tech professional enterprise integrating scientific research, production and sales.

S355J2 steel plate rolling process is controlled rolling process. In the rolling process, the ingot rolling temperature is 1000-1050℃; in the first stage, the low-speed and large reduction rolling process is adopted, the high-temperature stage is 950-1000℃, the S460QL steel equivalent rolling speed is 1.6-2.0m/s, the single reduction rate is 15-20%, and the cumulative reduction rate is 40-45%, so as to ensure sufficient deformation of ingot. In the first stage, the start rolling temperature is 910-930℃, and the finish rolling temperature is ≤ 870℃.As a basic building material, steel plates are currently widely used in automobiles, shipbuilding, chemical industry, aerospace and other fields. Reasonable selection of flaw detection methods to ensure the quality of S460QL steel equivalent steel plates is of great significance to safe production. Common defects of steel plates are folding, inclusion, shrinkage, air bubbles, delamination and cracks. These problems can be discovered in time through flaw detection.

The effect of nitrogen (N) on the properties of S460QL steel equivalent and so on steel is similar to that of carbon and phosphorus. With the increase of nitrogen content, the strength of steel can be significantly improved, especially the plasticity, especially toughness, and the weldability will be decreased, and the cold brittleness will be intensified. At the same time, aging tendency, cold brittleness and hot brittleness will be increased, which will damage the weldability and cold bending property of steel. Therefore, the nitrogen content in S460QL steel equivalent and so on steel should be reduced and limited as much as possible. Generally, nitrogen content should not be higher than 0.018%.

Our quality and service commitment: S460QL steel equivalent product quality problems, life-long replacement.In the process of using, any time if you find we supplied steel materials not conform to the requirements of technical standards, we can replace it for you free of charge. However, it should be noted that non product quality problems caused by improper use are not covered by the warranty. Please pay attention to the service time commitment as well as the product quality assurance commitment. Because only the products of big brands and reliable enterprises with complete after-sales service system can truly realize the long-term product quality assurance and the whole process of service.