S690QL properties for engineering

Q690E high strength steel
chemical composition: C: 0.08-0.15, Si: 0.17-0.37, Mn: 0.40-0.70, S: ≤0.035, P: ≤0.035, Cr: 0.30～0.60, Cu: ≤0.030, Ni: ≤0.030, V: 0.15-0.30, Mo: 0.25-0.35
Q690E mechanical properties: Tensile strength σb (MPa): ≥440 Yield strength σs (MPa): ≥225 Elongation δ5 (%): ≥22 Reduction of area ψ (%): ≥50 Impact energy Akv (J): ≥78

S690QL properties, Special thick steel plate cutting needs to be preheated in advance. Some steel plates are prone to cracks after entering the cutting process, sometimes that is because the temperature is too low, and it is necessary to perform pre-heat treatment in advance for such cases. The staff can preheat the steel plates first, so that the temperature of the steel plates will gradually increase, and then the flame gun can be used to cut. The probability of cracks in the cut material is very low, and the quality of the steel plate is also guaranteed.

Enterprise vision: to become a world-class innovation base and supplier of steel materials.Enterprise spirit: innovation, truth-seeking, integrity and efficiency.Core values of the enterprise: people-oriented, morality based, value creation, win-win sharing.Employee belief: have faith, can contribute; have dream, can fight; have action, can create; have value, can be happy.Employee belief: have faith, can contribute; have dream, can fight; have action, can create; have value, can be happy.

The blanking of the structural steel plate is first to find 90 degrees, and then use a tape measure and a powder line to draw the cutting range. According to the thickness of the carbon steel plate plus the cutting allowance, drilling is required. For the deep processing of S690QL properties structural steel sections or profiles: First use a square ruler or a curved ruler to find 90 degrees, and then use a square ruler or a ruler to cut the line and add the cutting margin to the hole.