Welcome to BBN High Strength Steels Factory

The iron oxide skin on surface of S960QL1 EN 10025-6 high strength steel

API2HGr50 delivery status: steel is usually delivered in hot rolled or hot forged state. It can also be delivered in the state of heat treatment (annealing, normalizing or high temperature tempering). Annealing: The steel S960QL1 EN 10025-6 high strength steel is heated to a suitable temperature and slowly cooled according to the heating time of different materials and specifications. Normalizing: Heat the steel plate to a suitable temperature and cool it in the air. Tempering: Keep the steel plate at an appropriate temperature for a long time while keeping it cool.

In today's S960QL1 EN 10025-6 high strength steel steel market, most of the varieties are in excess of demand, especially after China's accession to the WTO, steel enterprises are facing increasingly fierce market competition. In order to make enterprises win a good survival and development space, operators must make effective use of S960QL1 EN 10025-6 high strength steel market information resources to improve the scientificity of business decision-making and enhance the enterprises' domestic competitiveness Competitiveness in the external market.

S355J2 steel plate rolling process is controlled rolling process. In the rolling process, the ingot rolling temperature is 1000-1050℃; in the first stage, the low-speed and large reduction rolling process is adopted, the high-temperature stage is 950-1000℃, the S960QL1 EN 10025-6 high strength steel rolling speed is 1.6-2.0m/s, the single reduction rate is 15-20%, and the cumulative reduction rate is 40-45%, so as to ensure sufficient deformation of ingot. In the first stage, the start rolling temperature is 910-930℃, and the finish rolling temperature is ≤ 870℃.As a basic building material, steel plates are currently widely used in automobiles, shipbuilding, chemical industry, aerospace and other fields. Reasonable selection of flaw detection methods to ensure the quality of S960QL1 EN 10025-6 high strength steel steel plates is of great significance to safe production. Common defects of steel plates are folding, inclusion, shrinkage, air bubbles, delamination and cracks. These problems can be discovered in time through flaw detection.

Chromium element (Cr element) can improve the strength and hardness of S960QL1 EN 10025-6 high strength steel, carbon steel in rolling state, reduce elongation and area reduction. When the chromium content is more than 15%, the strength and hardness will decrease, while the elongation and reduction of area will increase correspondingly. It is easy to obtain high surface processing quality for steel parts containing chromium after grinding. The main function of chromium element (Cr element) in quenched and tempered steel structure is to improve hardenability, so that the steel has better comprehensive mechanical properties after quenching and tempering.

The after-sale service of iron and steel products includes after-sale tracking service, technical guidance, transfer of relevant bills, handling of objections and many other contents. The handling of quality objections accounts for a large proportion. When dealing with these problems, we should distinguish the responsibilities, and compensate or return the inconvenience or loss caused to users due to steel.

Tags:

Leave a Message

EN 10025-6 S690QL High Strength Steels